Product introduction
355X wax powder
Used for UV, solvent-based coating inks and powder coatings to improve surface smoothness and wear resistance.
Product Information
Chemical composition
Teflon modified polyethylene wax
Typical physicochemical data
The data provided on this data page is only typical values and not technical indicators of the product.
Melting point: 120/320℃
Particle size: D50: 4.5μm D90: 8μm
Supply form: Micronized powder
Storage and transportation
Storage in cool,dry or well-ventilated place.
Application
Liquid coating and inks
Product features and advantages
The additive can reduce the friction coefficient in solvent based coating inks, has excellent smoothness, and significantly improves the wear resistance and scratch resistance of the coating, and has good fineness. Can be used for abrasive free process.
Recommended Use
Iron printing coating, coil coating, floor coating, printing ink, wooding coating, plastic coating, UV coating.
Recommended dosage
0.3-3% additive dosage is based on the total formula, due to different formulations and process conditions, it is recommended to determine the best amount of addition before use.
Adding method and process guidance
The product can be directly dispersed in coatings and inks by high-speed stirring or grinding, and can also be added after preparation of wax paste.
Powder coatings
Features and advantages
The additive can improve the surface smoothness and scratch resistance, and improve the stain resistance of powder coatings.
Recommended dosage
0.3-2% additives based on the total formula, due to different formulations and process conditions, it is recommended to test before use to determine the best amount of addition.
Adding method and process guidance
The product is recommended to be added when the base material is premixed and then completely extruded. It can also be added to the sheet material mixed together with grinding and sifting, or added to the finished powder mixed and sifting.