357S Wax powder
Product introduction
357S wax powder
Used in UV, solvent-based paint inks and powder coatings to improve surface hardness and wear resistance.
Product Information
Chemical composition
Teflon modified polyethylene wax
Typical physicochemical data
The data provided on this data page is only typical values and not technical indicators of the product.
Melting point: 120/320℃
Particle size: D50: 6μm D90: 11μm
Supply form: Micronized powder
Storage and transportation
Storage in cool,dry or well-ventilated place.
Application
Liquid coating and inks
Product features and advantages
The additive can reduce the coefficient of friction in the solvent-based coating oil, has excellent smoothness, significantly improves the wear resistance and scratch resistance of the coating, and has good transparency.
Recommended Use
Wood coating, iron printing coating, coil coating, floor coating, printing ink, industrial coating, UV coating, plastic coating.
Recommended dosage
0.3-3% additive dosage based on the total formula. due to different formulations and process conditions. it is recommended to test before use to determine the best amount of addition.
Adding method and process guidance
The product can be directly dispersed in the coating and ink by high-speed stirring or grinding, and can also be added after preparation of wax paste.
Powder coatings
Features and advantages
The additive can improve the surface smoothness and scratch resistance, and improve the stain resistance of powder coatings.
Recommended dosage
0.3-2% additives based on the total formula, due to different formulations and process conditions, it is recommended to test before use to determine the best amount of addition.
Adding method and process guidance
The product is recommended to be added when the base material is premixed, and then completely extruded. It can also be added to the sheet material mixed together with grinding and sifting, or added to the finished powder mixed and sifting.